BMC/PBT plastic UV curing topcoat for vacuum metallization


Features

The product is high fullness of coating, good adhesion between interlayer、resistance to grinding、 corrosion、yellow and high temperature, and it is not easy to be whiten, with good tolerance for pitting dust.

 

Application

It can be applied in coating protection of car lights or decorative lighting fixtures、suitable for spraying operations and easy to operate.

 

Component

Aliphatic polyurethane oligomers, acrylic monomers, cosolvents, initiators.

 

Points for Operation

Metallization components - Spray coating - Let stand (3-5 minutes) - Infrared (3-5 minutes) - Exposure (600-800mj/c㎡)

This product can be directly sprayed and can be mixed with a special diluent if there are special requirements. It should achieve cumulative light exposure and use a multi angle UV machine for polyhedral work-pieces. This product is low viscosity and need to concern thickness of the spray film to avoid sagging. The already metalized work-piece should be coated with a topcoat within 4 hours. Otherwise, it will affect the adhesion.

 

Precautions

The quality guarantee period for this product is 6 months. If it expires, please test its applicability. Please seal the unused paint and store it in a dark, ventilated, and dry place. Spraying operation tools, containers, etc. should be cleaned with special cleaning agents. The designated diluent must be used for dilution. The product should be stored in a dry, cool, and ventilated place. The product should be transported in undamaged original cans.

 

 

Data of BMC/PBT plastic UV curing topcoat for vacuum metallization series

Item

Index

Test Standard

Appearance and color of paint film

Smooth and flat、consistent with the sample

GB/9761-1988

Viscosity (Paint 4 Cups, 25 ℃)

11~12 Second

GB/T1723-1993

Grind Fineness

≤15μm

GB/T1724-1989

Gloss (60 ℃)

≥90

GB/T9754-1988

Adhesion/Grade (Cross Cut)

100/100 (3M610#Tape)

GB/T9286-1998

Pencil Hardness

2H (Zhonghua Pencil)

GB/T6739-1996

Resistance to Grind

350 Times (175g/RCA)

175g/RCA

Excellent chemical resistance

Soak  in 0.1N H2SO4 and 0.1N NaOH solutions for 24 hours without any changes

GB/T1763-1989

Resistance to Humidity & Heat

72HR(90%-65 ℃) Blistering, wrinkles
, rust, or obvious fading are not founded

GB/T1765-1989

Salt spray Resistance 48h

Line rust width ≤3mm, 2mm outside  scratch distance No abnormal

GB/T1765-1989

Resistance to High & Low Temperature

72HR(-40~75 ℃), Others no significant changes

-40~75 ℃

Heavy Metal Content

Complies with international toy safety standards、the CPSC standards of the US Consumer Product Safety Commission and the European RoHS directive standards

ASTM

F963-96A
RoHS

 